Sensitivity of the Creep-Rupture Properties of Waspaloy Sheet to Sharp-Edged Notches in the Temperature Range 1000–1400 Deg F

[+] Author and Article Information
D. J. Wilson

Department of Materials and Metallurgical Engineering, University of Michigan, Ann Arbor, Mich.

J. Basic Eng 94(1), 13-21 (Mar 01, 1972) (9 pages) doi:10.1115/1.3425343 History: Received July 30, 1971; Online October 27, 2010

Abstract

Time-dependent notch sensitivity of Waspaloy was observed at test temperatures from 1000 to 1300 deg F. Its occurrence in this range was dependent on the heat treatment. “Overaging” eliminated the notch sensitivity. Optimum combination of smooth and notched specimen strengths for material solution treated at 1975 deg F were obtained by aging 24 hr at 1550 deg F. Necessary conditions for time-dependent notch sensitivity were (i) the notch specimen loads had to be below the approximate 0.2 percent off set yield strength; and (ii) test data from smooth specimens had to indicate that small amounts of creep used up large fractions of creep-rupture life. No reasons were evident why these criteria will not prove applicable to other alloys.

Copyright © 1972 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In